With excellent thermo forming properties, Day Might-H and Day Might-M are high performance PVC films, which conform to USP/EC/REACH guidelines. The high-gloss, deep draw properties and high impact strength, coupled with clarity make it an ideal choice for a wide range of applications.
Properties that give you the mighty edge :-
Good impact strength
Excellent formability
Higher processing yields
Excellent clarity & transparency
High release properties
Low crease whitening
Complying to EEC/USP guidelines (current version)
Wide range, suitable for deep draw and medium draw applications
Customized variants of anti-static films & UV grade films
Seals reliably - using RF, heat or ultrasonic methods
Fenoplast Films are Manufactured in a Controlled Environment Following Good Manufacturing Practices.
Technical Data :-
SL. NO.
CHARACTERISTICS
UNIT
METHOD
SPECIFICATION & REMARKS
1
Thickness Tolerance
MICRONS
DIN 53370
± 10% for <_200; ± 8% for 201 to 400; ± 4% for 401 to 700
2
GSM Tolerance
GM/M²
DIN 53352
± 10% for <_200; ± 8% for 201 to 400; ± 4% for 401 to 700
3
Gloss (@20°C)
%
ASTM D 2457
Day Might-H : Min. 110- for Transparent Film
Day Might-M : Min. 100- for Transparent Film
4
Impact Strength
GM
ASTM D 1709
For > 250µ - 500 Min.
For < 220µ - 350 Min.
5
Dimensional Stability
(@ 1400°C/10 min)
% MD
DIN 53377
-3.0 to -13.0(110 to 170µ), -3.0 to -10.0(171 to 200µ)
-3.0 to -8.0(201 to 250µ), -3.0 to -7.0(>250µ)
%TD
DIN 53377
0.5 to 6.0(110 to 170µ), 0.5 to 5.0(171 to 200µ)
0.5 to 4.0(201 to 250µ), 0.5 to 2.5(>250µ)
6
Tensile Strength at Peak
KG/CM²
ASTM D 882
Day Might-H : >_ 400, Day Might-M : >_450
7
Elongation at Peak Load (Jaw Separation Speed @20mm/min)
%
ASTM D 882
_>4
8
Density
GM/CM³
ASTM -D 792
Day Might-H : 1.33 ± 0.02 Tr. Film,1.36 ± 0.02 OP Film
Day Might-M : 1.34 ± 0.02 Tr.Film,1.37 ± 0.02 OP Film
9
Vicat Softening Point
°C
ASTM -D 1525
74 ± 2
10
WVTR @ 38°C, 90% RH
GM/M²/24HR
ASTM F 1249
< 4.00(<_200µ); <3.75(>220µ)
11
OTR @ 23°C, 0% RH
CM³/M²/24HR
ASTM D 3985
< 12.00(<_200µ); <10.00(>220µ)
12
Toxicity
N/A
Current USP Method
Non - Toxic
13
Global Migration
PPM
2002/72/EC
< 10
14
RVCM Content
PPM
78/142/EEC
< 0.50
15
RoHS
PPM
94/62/EC
Complies
16
Other Defects
N/A
FPL/QA/STP-17
Free from Air Streaks, Dents, Hot Patches
These technical specifications and end-use recommendations are based on our observations and assessment.
Validating/optimizing the right grade may vary based on particular application, tooling and process conditions.